［GENERAL INFORMATION］

CMAX high alumina firebricks are classified according to alumina content ranging from 48% to 95%, manufactured from such mineral as bauxite, corundum, etc. by mixing, press-forming, drying, sintering and machining. CMAX high alumina bricks feature stable mechanical strength and thermal shock resistance, with high refractoriness of no lower than 1880℃.

CMAX high alumina bricks are commonly used as refractory lining exposed to heat directly or backup insulation linings in various types of industrial kiln or laboratory furnace.

［ADVANTAGES］

Low thermal conductivity

High refractoriness

Excellent acid and base slagging resistance

Excellent thermal shock resistance

Excellent mechanical strength

Non standard sizes and shapes are available upon request.

［APPLICATIONS］

Blast furnace

Hot-blast stove

Annealing furnace

Laboratory furnace

Cement kiln

Electric stove roof and ladle backup layer

Physical Properties:

Classification Temperature, ℃ ----1790

Apparent Porosity,% ----22

C.C.R. Strength, MPa ----49

Hot Load Strength Deform(0.2MPa) ----1500℃

Reheating Linear Change (1500℃, 2 h),% ----+0.1 ~ -0.4

Chemical analysis:

Al2O3, % ----65

Fe3O3, % ----2.0