Aggregates 
Unshaped Refractories for Rotary Kiln
|
CODE |
PYSICAL PROPERTIES |
CHEMICAL ANALYSIS (WEIGHT %) |
||||||
|
B.D. (g/cm3) |
R.L.C. (1100*3h) % |
C.C.S (Mpa) |
M.W.T. (℃) |
W.A (%) |
Al2O3+SiC (%) |
Al2O3 (%) |
SiC (%) |
|
|
C13NL |
2.10 |
±0.4 |
70 |
1300 |
6.5-7.5 |
90 |
48 |
50 |
|
C14NL |
2.20 |
±0.4 |
70 |
1400 |
6-7 |
80 |
48 |
50 |
|
C16T |
2.65 |
±0.3 |
100 |
1600 |
5.5-6.5 |
70 |
75 |
|
|
C16 |
2.60 |
±0.4 |
100 |
1600 |
6.0-7.5 |
|
70 |
|
|
C160 |
2.70 |
±0.4 |
100 |
1600 |
5.5-6.0 |
|
75 |
|
|
C15B |
2.60 |
±0.4 |
80 |
1500 |
5.5-6.5 |
|
70 |
|
|
C18S |
3.00 |
±0.3 |
150 |
1750 |
4.5-5.0 |
|
65 |
|
|
C80MC |
2.90 |
±0.3 |
100 |
1600 |
4.5-5.5 |
|
25-30 |
|
|
C70MC |
2.75 |
±0.3 |
100 |
1600 |
5.5-6.5 |
90 |
5.0 |
|
Unshaped Refractories for Preheater/Kiln Hood/Calciner/Teriaty Air Duct/Cooler
|
CODE |
PYSICAL PROPERTIES |
CHEMICAL ANALYSIS (WEIGHT %) |
||||||
|
B.D. (g/cm3) |
R.L.C. (1100*3h) % |
C.C.S (Mpa) |
M.W.T. (℃) |
W.A (%) |
Al2O3+SiC (%) |
Al2O3 (%) |
SiC (%) |
|
|
C13NL |
2.10 |
±0.4 |
70 |
1300 |
6.5-7.5 |
90 |
48 |
50 |
|
C14NL |
2.20 |
±0.4 |
70 |
1400 |
6-7 |
80 |
48 |
50 |
|
C16T |
2.65 |
±0.3 |
100 |
1600 |
5.5-6.5 |
70 |
75 |
|
|
C16 |
2.60 |
±0.4 |
100 |
1600 |
6.0-7.5 |
|
70 |
|
|
C160 |
2.70 |
±0.4 |
100 |
1600 |
5.5-6.0 |
|
75 |
|
|
C15B |
2.60 |
±0.4 |
80 |
1500 |
5.5-6.5 |
|
70 |
|
|
C18S |
3.00 |
±0.3 |
150 |
1750 |
4.5-5.0 |
|
65 |
|
|
C80MC |
2.90 |
±0.3 |
100 |
1600 |
4.5-5.5 |
|
25-30 |
|
|
C70MC |
2.75 |
±0.3 |
100 |
1600 |
5.5-6.5 |
90 |
5.0 |
|
Note: B.D is short for Bulk Density
A.P is short for Apparent Porosity
C.C.S is short for Cold Crushing Strength
R.U.L is short for Refractoriness Under Load
T.E. is short for Thermal Expansion
W.A. is short for Water Addition
M.S.T. is short for Max. Service Temperature