Aggregates REFRACTORIES FOR ROTARY KILN
|
Application |
Materials |
Code |
|
Outlet Zone |
High Strength Abrasion Resistant Corundrum-Mullite Castable |
C18S |
|
C80MC |
||
|
Upper & Lower Transition Zone |
Magnesia-MA Spinel Brick |
MA-85A |
|
MA-85B |
||
|
MA-85C |
||
|
MA-93A |
||
|
MA-93B |
||
|
Silica Mullite Brick |
SM1650 |
|
|
SM1680 |
||
|
Phosphate Bonded High Alumina Brick |
P75 |
|
|
Burning Zone |
Directly Bonded Magnesia-Chrome Brick |
DMC-8A |
|
DMC-8B |
||
|
DMC-9A |
||
|
Magnesia Hercynite Brick |
MFe-80 |
|
|
MFe-85 |
||
|
MFe-90 |
||
|
Magnesia Alumina Zirconia Lanthana Brick |
MAZL-90 |
|
|
Calcining Zone |
Spalling Resistant High Alumina Brick |
YRS-70 |
|
AL-75A |
||
|
AL-75B |
||
|
AL-80A |
||
|
AL-80B |
||
|
High Strength Alkali Resistant Brick |
RK-H |
|
|
Phosphate Bonded High Alumina Brick |
P75 |
|
|
Inlet Zone |
High Alumina Low Cement Castable |
C16 |
Physical and Chemical Properties for Shaped Refractories
|
CODE |
PYSICAL PROPERTIES |
CHEMICAL ANALYSIS (WEIGHT %) |
||||||||
|
B.D. (g/cm3) |
A.P. % |
C.C.S. (Mpa) |
R.U.L. (T0.6,℃) |
T.E (%) |
MgO (%) |
Fe2O3 (%) |
Al2O3 (%) |
SiO2 (%) |
Cr2O3 (%) |
|
|
MA-85A |
2.95 |
18 |
50 |
1700 |
1.2 |
85 |
|
8.0 |
1.0 |
|
|
MA-85B |
2.90 |
18 |
45 |
1700 |
1.2 |
82 |
|
8.0 |
2.0 |
|
|
MA-85C |
2.85 |
19 |
40 |
1650 |
1.2 |
80 |
|
8.0 |
3.0 |
|
|
MA-93A |
2.95 |
18 |
45 |
1700 |
1.5 |
93 |
|
5.0 |
1.0 |
|
|
MA-93B |
2.90 |
18 |
40 |
1700 |
1.5 |
90 |
|
5.0 |
2.0 |
|
|
MFe-80 |
2.90 |
17 |
45 |
1550 |
1.6 |
80 |
7.5 |
|
2.0 |
|
|
MFe-85 |
3.00 |
17 |
50 |
1600 |
1.6 |
85 |
7.5 |
|
1.0 |
|
|
MFe-90 |
2.85 |
16 |
50 |
1650 |
1.7 |
90 |
4.5 |
|
1.5 |
|
|
DMC-8A |
3.00 |
17 |
40 |
1700 |
1.5 |
82 |
|
|
1.5 |
8.0 |
|
DMC-8B |
2.95 |
18 |
45 |
1650 |
1.5 |
76 |
|
|
2.0 |
8.0 |
|
DMC-9A |
3.00 |
19 |
40 |
1600 |
1.6 |
70 |
|
|
2.8 |
9.0 |
|
YRS-70 |
2.55 |
25 |
60 |
1470 |
1.7 |
|
|
70 |
|
|
|
AL-75A |
2.70 |
20 |
70 |
1500 |
|
|
1.7 |
75 |
|
|
|
AL-75B |
2.65 |
20 |
55 |
1500 |
|
|
1.7 |
75 |
|
|
|
AL-80A |
2.80 |
20 |
80 |
|
0.9 |
|
1.5 |
80 |
|
|
|
AL-80B |
2.70 |
20 |
70 |
|
|
|
1.5 |
80 |
|
|
|
SM1650 |
2.65 |
20 |
95 |
1650 |
|
|
|
65 |
30 |
|
|
SM1680 |
2.65 |
18 |
90 |
1680 |
|
|
|
65 |
30 |
|
|
RK-H |
|
20 |
60 |
1300 |
0.70 |
|
|
25-30 |
60-70 |
|
|
MAZL90 |
2.95 |
18 |
50 |
1700 |
1.5 |
90 |
|
5.0 |
1.0 |
|
|
P75 |
2.65 |
|
60 |
1300 |
|
|
3.2 |
75 |
|
|
Physical and Chemical Properties for Unshaped Refractories
|
CODE |
PYSICAL PROPERTIES |
CHEMICAL ANALYSIS (WEIGHT %) |
||||||
|
B.D. (g/cm3) |
R.L.C. (1100*3h) % |
C.C.S (Mpa) |
M.W.T. (℃) |
W.A (%) |
Al2O3+SiC (%) |
Al2O3 (%) |
SiC (%) |
|
|
C13NL |
2.10 |
±0.4 |
70 |
1300 |
6.5-7.5 |
90 |
48 |
50 |
|
C14NL |
2.20 |
±0.4 |
70 |
1400 |
6-7 |
80 |
48 |
50 |
|
C16T |
2.65 |
±0.3 |
100 |
1600 |
5.5-6.5 |
70 |
75 |
|
|
C16 |
2.60 |
±0.4 |
100 |
1600 |
6.0-7.5 |
|
70 |
|
|
C160 |
2.70 |
±0.4 |
100 |
1600 |
5.5-6.0 |
|
75 |
|
|
C15B |
2.60 |
±0.4 |
80 |
1500 |
5.5-6.5 |
|
70 |
|
|
C18S |
3.00 |
±0.3 |
150 |
1750 |
4.5-5.0 |
|
65 |
|
|
C80MC |
2.90 |
±0.3 |
100 |
1600 |
4.5-5.5 |
|
25-30 |
|
|
C70MC |
2.75 |
±0.3 |
100 |
1600 |
5.5-6.5 |
90 |
5.0 |
|
Note: B.D is short for Bulk Density
A.P is short for Apparent Porosity
C.C.S is short for Cold Crushing Strength
R.U.L is short for Refractoriness Under Load
T.E. is short for Thermal Expansion
W.A. is short for Water Addition
M.S.T. is short for Max. Service Temperature
REFRACTORIES FOR PREHEATER/KILN HOOD/CALCINER/TERIATY AIR DUCT/COOLER
|
Application |
Materials |
Code |
|
Preheater |
Alkali Resistant Castable |
C13NL |
|
C14NL |
||
|
Alkali Resistant Brick |
RK-O |
|
|
RK-H |
||
|
RK-A |
||
|
CB-20 |
||
|
CB-30 |
||
|
Kiln Hood |
High Strength Corndum-Mullite Castable |
C18S |
|
C80MC |
||
|
C70MC |
||
|
High Alumina Low Cement Castable |
C16T |
|
|
C16 |
||
|
C160 |
||
|
C15B |
||
|
Calciner |
Spalling Resistant High Alumina Brick |
YRS-70 |
|
AL-75A |
||
|
AL-75B |
||
|
AL-80A |
||
|
AL-80B |
||
|
High Alumina Low Cement Castable |
C16T |
|
|
C16 |
||
|
C160 |
||
|
C15B |
||
|
Tertiary Air Duct |
Alkali Resistant Castable |
C13NL |
|
C14NL |
||
|
Silica-Mullite Brick |
SM1650 |
|
|
SM1680 |
||
|
Cooler |
Alkali Resistant Castable |
C13NL |
|
C14NL |
||
|
High Alumina Low Cement Castable |
C16T |
|
|
C16 |
||
|
C160 |
||
|
C15B |
Physical and Chemical Properties for Shaped Refractories
|
CODE |
PYSICAL PROPERTIES |
CHEMICAL ANALYSIS (WEIGHT %) |
||||||
|
B.D. (g/cm3) |
A.P. % |
C.C.S. (Mpa) |
R.U.L. (T0.6,℃) |
T.E (%) |
Fe2O3 (%) |
Al2O3 (%) |
SiO2 (%)
|
|
|
YRS-70 |
2.55 |
25 |
60 |
1470 |
1.7 |
|
70 |
|
|
AL-75A |
2.70 |
20 |
70 |
1500 |
|
1.7 |
75 |
|
|
AL-75B |
2.65 |
20 |
55 |
1500 |
|
1.7 |
75 |
|
|
AL-80A |
2.80 |
20 |
80 |
|
0.9 |
1.5 |
80 |
|
|
AL-80B |
2.70 |
20 |
70 |
|
|
1.5 |
80 |
|
|
SM1650 |
2.65 |
20 |
95 |
1650 |
|
|
65 |
30 |
|
SM1680 |
2.65 |
18 |
90 |
1680 |
|
|
65 |
30 |
|
RK-O |
|
25 |
25 |
1350 |
0.70 |
|
25-30 |
60-70 |
|
RK-H |
|
20 |
60 |
1300 |
0.70 |
|
25-30 |
60-70 |
|
RK-A |
|
25 |
30 |
1400 |
0.65 |
|
30-35 |
60-65 |
|
CB-20 |
|
30 |
15 |
1250 |
0.60 |
|
25-30 |
60-67 |
|
CB-30 |
|
30 |
20 |
1250 |
0.60 |
|
25-30 |
60-67 |
Physical and Chemical Properties for Unshaped Refractories
|
CODE |
PYSICAL PROPERTIES |
CHEMICAL ANALYSIS (WEIGHT %) |
||||||
|
B.D. (g/cm3) |
R.L.C. (1100*3h) % |
C.C.S (Mpa) |
M.W.T. (℃) |
W.A (%) |
Al2O3+SiC (%) |
Al2O3 (%) |
SiC (%) |
|
|
C13NL |
2.10 |
±0.4 |
70 |
1300 |
6.5-7.5 |
90 |
48 |
50 |
|
C14NL |
2.20 |
±0.4 |
70 |
1400 |
6-7 |
80 |
48 |
50 |
|
C16T |
2.65 |
±0.3 |
100 |
1600 |
5.5-6.5 |
70 |
75 |
|
|
C16 |
2.60 |
±0.4 |
100 |
1600 |
6.0-7.5 |
|
70 |
|
|
C160 |
2.70 |
±0.4 |
100 |
1600 |
5.5-6.0 |
|
75 |
|
|
C15B |
2.60 |
±0.4 |
80 |
1500 |
5.5-6.5 |
|
70 |
|
|
C18S |
3.00 |
±0.3 |
150 |
1750 |
4.5-5.0 |
|
65 |
|
|
C80MC |
2.90 |
±0.3 |
100 |
1600 |
4.5-5.5 |
|
25-30 |
|
|
C70MC |
2.75 |
±0.3 |
100 |
1600 |
5.5-6.5 |
90 |
5.0 |
|
Note: B.D is short for Bulk Density
A.P is short for Apparent Porosity
C.C.S is short for Cold Crushing Strength
R.U.L is short for Refractoriness Under Load
T.E. is short for Thermal Expansion
W.A. is short for Water Addition
M.S.T. is short for Max. Service Temperature